Abstract
LiFePO4 was prepared via high temperature solid-state method at different heat preservation time. XRD and SEM was used to test the structure and morphology of LiFePO4. Land 2001 was used to test the electrochemical performance of LiFePO4. The results illustrated that well-crystallized LiFePO4 composite with homogeneous small particles was obtained by XRD and SEM. And the optimum heat preservation time was 4 hour. From charge/discharge test, it can be seen that at 0.2C, LiFePO4 has initial discharge capacities of 159.1mAh/g at the heat preservation time 4 hour. From the rate capacity, it can be seen that the discharge capacity was of optimum sample remains above 99% after 200 cycles.