Abstract
Hydroxyapatite (Ca10 (PO4)6(OH)2, HA), is an attractive material of an inorganic compound whose chemical composition and crystallographic structures are similar to the composition of the bone. A natural source such as egg shells is composed of 94 wt. % of calcium carbonate (CaCO3), which can be calcined as calcium oxide (CaO) by the calcinations process. The efficient temperature to produce CaO is 900 °C for 2 hours. The synthesis of nano-HA was done by the mixing the diammonium phosphate (DAP) and calcium hydroxide (Ca(OH)2) and subjected into a microwave for 30 minutes at 1100 W irradiation power. Ball milling process was used for 30 minutes to mix the nano-HA with different compositions of titanium. These were pressed to form pallets by hand hydraulic pump (force=2300 psi). The pallets then were sintered at 1200 °C with the heating rate of 3 °C/min for 2 hours. The pallets were tested by several mechanical testing including hardness, compression strength and wear. From the results, HA-25wt. %Ti composite gave the highest hardness, compression and coefficient of friction for wear test values which were 89.6 Hv, 82.5MPa and 0.76μ respectively. It showed that by adding Ti to nano-HA, the mechanical properties of nano-HA could be enhanced. The microstructure analyses by optical micrograph showed that nano-HA-Ti particles displayed shape likes needle morphology. The particles showed the high tendency to form the agglomerations.
Export citation and abstract BibTeX RIS
Content from this work may be used under the terms of the Creative Commons Attribution 3.0 licence. Any further distribution of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI.