Abstract
Manganese dioxide (MnO2) nanoflakes were effectively produced at ambient temperature using a solution technique. The SEM, XRD, BET, and electrochemical tests were used to investigate the characteristics of the produced materials (MnO2). The XRD pattern of the manganese oxide sample obtained reveals that it possesses crystal structure. The morphology was examined using a scanning electron microscope image, which confirmed the development of nanoflakes in the 70-100 nm diameter range. The higher specific capacitance achieves 200 Fg-1 at current density and at scan rate of 0.5 A/g and 5 mv/s respectively. For the highest specific capacitance, the obtained value of power density and energy density are of 257.14 w/kg and 25 w.h/kg respectively.