Abstract
Preparing fine tungsten particles tungsten heavy alloys (WHAs) is a method to improve the susceptibility to adiabatic shear of WHAs. In this paper, W-AlCrFeNiV alloy (W-HEA) with different size W particles were prepared by laser ultrashort-time liquid phase sintering (LULPS) and liquid phase sintering (LPS). The effects of W particle size of W-HEA on mechanical property and susceptibility to adiabatic shear are studied. The results show that W-HEA with 3 μm W particles has excellent mechanical properties-tensile strength nearly 1500 MPa. The tensile strength is 58% higher than that W-HEA with 20 μm W particle. W-HEA with 3 μm W particle dynamic compression strength is 2200 MPa under 4000 s-1. The dynamic strength is 22% higher than that tungsten heavy alloy with 20 μm W particle. And the smaller W particles are, the stronger susceptibility to adiabatic shear is. The adiabatic shear band width of W-HEA with 3 μm W particles is 10 μm after dynamic compression.
Export citation and abstract BibTeX RIS
Content from this work may be used under the terms of the Creative Commons Attribution 3.0 licence. Any further distribution of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI.