Synthesis, Characterization, and NH₃ Sensing Properties of (Zn_0.7 Mn_0.3-x Ce_x Fe₂O₄) Nano-Ferrite

This study includes the preparation of novel nano ferrite (Zn_0.7 Mn_0.3-x Ce_x Fe₂O₄) by using the auto combustion technique. For the following molar values, the percentage x was calculated: 0.0, 0.05, 0.1, 0.15, 0.2, 0.25, and 0.3. The nano-ferrite was calcined for 2 hours at 500°C. The energy dispersive x-ray spectroscopy (EDX), X-ray diffraction (XRD) and field emission scanning electron microscopy FE-SEM was used to examine structural, morphological, and sensing properties. The spinel cubic structure was revealed by XRD findings. The particle distribution was shown to contain voids by FE-SEM. The testing of sensing characteristics to NH3 gas indicated that the synthesized nano-ferrite has a small response time ranging from (15.3-25.2) s as well as a small recovery time between (36-58.5) s, also has a higher sensitivity of about 72.23%.