Abstract
Nano ferrite with chemical formula (Ni0.35Cu0.2Zn0.45LaxFe2-xO4), were chemically collected utilizing sol-gel auto – combustion procedure for the values of (X=0.0, 0.025, 0.05 and 0.075). The prepared samples were calcined at (900°C) for (2h), the formation of ferrite was assured using (XRD) and (SEM) techniques. X-ray diffractometer result shows that ferrite have spinal cubic phase with a particle size ranging from (22-29 nm),the Lattice constant and density (ρx-ray) increased with La+3content while the porosity was noticed to decrease. And have been studied dielectric properties It was also observed that the value of the dielectric constant and the dielectric loss factor decreased by increasing the frequency. The increase in alternating conductivity (σa.c) was also observed with increasing frequency.
Export citation and abstract BibTeX RIS
Content from this work may be used under the terms of the Creative Commons Attribution 3.0 licence. Any further distribution of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI.