Plasma-spray technology is under investigation as a method for producing high thermal conductivity beryllium coatings for use in magnetic fusion applications. Recent investigations have focused on optimizing the plasmaspray process for depositing beryllium coatings on damaged beryllium surfaces. Of particular interest has been optimizing the processing parameters to maximize the through-thickness thermal conductivity of the beryllium coatings. Experimental results will be reported on the use of secondary H2 gas additions to improve the melting of the beryllium powder and negative transferred-arc cleaning to improve the bonding between the beryllium coatings and the underlying surface. Information will also be presented on thermal cycle tests which were done on beryllium coated ISX-B beryllium limiter tiles using 10s cycle times with 60s cooldowns using a heat flux slightly in excess of 5 MW/m2.