Abstract
This paper discusses the effects of heating temperatures of 200°C, 400°C and 600°C each for 2 hours at a heating rate of 2.5°C/min on concrete with the content of Natural Coarse Aggregates (NCA) partially replaced with Recycled Coarse Aggregates (RCA), obtained from demolished building in the ratio of 0%, 15% and 30%.There was an initial drop in strength from 100°C to 200°C which is suspected to be due to the relatively weak interfacial bond between the RCA and the hardened paste within the concrete matrix;a gradual increase in strength continued from 200°C to 450°C and steady drop occurred again as it approached 600°C.With replacement proportion of 0%, 15% and 30% of NCA and exposure to peak temperature of 600°C, a relative concrete strength of 23.6MPa, 25.3MPa and 22.2MPa respectively can be achieved for 28 days curing age. Furthermore, RAC with 15% NCA replacement when exposed to optimum temperature of 450°C yielded high compressive strength comparable to that of control specimen (normal concrete). In addition, for all concrete samples only slight surface hairline cracks were noticed as the temperature approached 400°C. Thus, the RAC demonstrated behavior just like normal concrete and may be considered fit for structural use.
Export citation and abstract BibTeX RIS
Content from this work may be used under the terms of the Creative Commons Attribution 3.0 licence. Any further distribution of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI.