Abstract
CdTe and CZT detectors are considered better choices for high energy γ and X-ray spectroscopy in comparison to Si and HPGe detectors due to their good quantum efficiency and room temperature operation. The performance limitations in CdTe and CZT detectors are mainly associated with poor hole transport and trapping phenomena. Among many techniques that can be used to eliminate the effect of the poor charge transport properties of holes in CdTe and CZT material, the drift ring technique shows promising results. In this work, the performance of a 2.3 mm thick CZT drift ring detector is investigated. Spatially resolved measurements were carried out with an X-ray microbeam (25 and 75 keV) at the Diamond Light Source synchrotron to study the response uniformity and extent of the active area. Higher energy photon irradiation was also carried out at up to 662 keV using different radioisotopes to complement the microbeam data. Different biasing schemes were investigated in terms of biasing the cathode rear electrode (bulk field) and the ring electrodes (lateral fields). The results show that increasing the bulk field with fixed-ratio ring biases and lateral fields with fixed bulk fields increase the active area of the device significantly, which contrasts with previous studies in CdTe, where only an increasing lateral field resulted in an improvement of device performance. This difference is attributed to the larger thickness of the CZT device reported here.