In this work, the aging damping associated with the discontinuous phase transformation was studied in two Al-Zn alloys using a forced-vibration pendulum. Correlating these results with an X-ray diffraction analysis and TEM observations the authors suggested that the aging damping was directly proportional to the total interface area which was related to the nucleation and growth during the discontinuous transformation.