A P Menushenkov et al 2009 J. Phys.: Conf. Ser. 190 012091 doi:10.1088/1742-6596/190/1/012091
A P Menushenkov1, V P Menushenkov2, R V Chernikov1, T A Sviridova2, O V Grishina1, V V Sidorov1 and K V Klementiev3
Show affiliationsLocal crystalline structure of hypo- and hyperstoichiometric SmCox alloys with x = 5.15, 4.95, 4.0, 3.75 heat treated in different conditions was investigated by means of the X-ray absorption spectroscopy. Experimental spectra were measured above the L3-Sm absorption edge. EXAFS-analysis shows that stacking faults appear in hyperstoichiometric alloys SmCo4 and SmCo3.75, confirming the hypothesis of "high coercive state, induced by phase transformations, changing the state of the grain surface in basic phase". L3-Sm XANES spectra demonstrate the reduction of the "white line" amplitude in Sm-enriched samples.
61.05.cj X-ray absorption spectroscopy: EXAFS, NEXAFS, XANES, etc.
78.70.Dm X-ray absorption spectra
75.50.Vv High coercivity materials
61.72.Nn Stacking faults and other planar or extended defects
75.60.Ej Magnetization curves, hysteresis, Barkhausen and related effects
Issue 1 (2009)
A P Menushenkov et al 2009 J. Phys.: Conf. Ser. 190 012091
Seong Jun Kim et al 2009 Smart Mater. Struct. 18 115009
Joseph Ben Geloun and Mahouton Norbert Hounkonnou 2009 J. Phys. A: Math. Theor. 42 295202
Julien Tailleur et al 2008 J. Phys. A: Math. Theor. 41 505001
Sunnyeo Lee et al 2009 Class. Quantum Grav. 26 245002
H George et al 2009 New J. Phys. 11 113028
Martina Roso et al 2008 Nanotechnology 19 285707
Fu Yong-Ping and Li Yun-De 2009 Chinese Phys. Lett. 26 111201
G L Gattobigio et al 2010 Phys. Scr. 81 025301
L Assoud et al 2009 J. Phys.: Condens. Matter 21 464114